There are two principal neodymium magnet manufacturing routes:

• The classical powder metallurgy or sintered magnet process
• The rapid solidification or bonded magnet process

Sintered Nd-magnets are prepared by the raw materials being melted in a furnace, cast into a mold and cooled to form ingots. The ingots are pulverized and milled to tiny particles. This undergoes a process of liquid-phase sintering whereby the powder is magnetically aligned into dense blocks which are then heat-treated, cut to shape, surface treated and magnetized. Currently, between 45,000 and 50,000 tons of sintered neodymium magnets are produced each year, mainly in China and Japan. As of 2011, China produces more than 95% of rare earth elements, and produces 76% of the world's total rare earth magnets.

Bonded Nd-magnets are prepared by melt spinning a thin ribbon of the Nd-Fe-B alloy. The ribbon contains randomly oriented Nd₂Fe₁₄B nano-scale grains. This ribbon is then pulverized into particles, mixed with a polymer and either compression or injection molded into bonded magnets. Bonded magnets offer less flux than sintered magnets but can be net-shape formed into intricately shaped parts and do not suffer significant eddy current losses. There are approximately 5,500 tons of Neo bonded magnets produced each year. In addition, it is possible to hot-press the melt spun nanocrystalline particles into fully dense isotropic magnets, and then upset-forge/back-extrude these into high-energy anisotropic magnets.