Mail (armour) - Manufacture

Manufacture

Several patterns of linking the rings together have been known since ancient times, with the most common being the 4-to-1 pattern (where each ring is linked with four others). In Europe, the 4-to-1 pattern was completely dominant. Mail was also common in East Asia, primarily Japan, with several more patterns being utilised and an entire nomenclature developing around them.

Historically, in Europe, from the pre-Roman period on, the rings composing a piece of mail would be riveted closed to reduce the chance of the rings splitting open when subjected to a thrusting attack or a hit by an arrow.

Up until the 14th century European mail was made of alternating rows of riveted rings and solid rings. After that point mail was almost all made from riveted rings only. Both were commonly made of wrought iron, but some later pieces were made of heat-treated steel. Wire for the riveted rings was formed by either of two methods. One was to hammer out wrought iron into plates and cut or slit the plates. These thin pieces were then pulled through a draw plate repeatedly until the desired diameter was achieved. Waterwheel powered drawing mills are pictured in several period manuscripts. Another method was to simply forge down an iron billet into a rod and then proceed to draw it out into wire. The solid links would have been made by punching from a sheet. Guild marks were often stamped on the rings to show their origin and craftsmanship. Forge welding was also used to create solid links, but there are few possible examples known, the only well documented example from Europe is that of the 7th century Coppergate mail drape. Outside of Europe this practice was more common such as "theta" links from India. Very few examples of historic butted mail have been found and it is generally accepted that butted mail was never in wide use historically except in Japan where mail (kusari) was commonly made from butted links.