The Knoop hardness test ( /kǝˈnuːp/) is a microhardness test - a test for mechanical hardness used particularly for very brittle materials or thin sheets, where only a small indentation may be made for testing purposes. A pyramidal diamond point is pressed into the polished surface of the test material with a known force, for a specified dwell time, and the resulting indentation is measured using a microscope. The geometry of this indenter is an extended pyramid with the length to width ratio being 7:1 and respective face angles are 172 degrees for the long edge and 130 degrees for the short edge. The depth of the indentation can be approximated as 1/30 of the long dimension. The Knoop hardness HK or KHN is then given by the formula:
where:
- L = length of indentation along its long axis
- Cp = correction factor related to the shape of the indenter, ideally 0.070279
- P = load
HK values are typically in the range from 100 to 1000, when specified in the conventional units of gf·mm−2. The SI unit, pascals, are sometimes used instead: 1 kgf·mm−2 = 9.80665 MPa.
The test was developed by Frederick Knoop and colleagues at the National Bureau of Standards (now NIST) of the USA in 1939, and is defined by the ASTM E384 standard.
The advantages of the test are that only a very small sample of material is required, and that it is valid for a wide range of test forces. The main disadvantages are the difficulty of using a microscope to measure the indentation (with an accuracy of 0.5 micrometre), and the time needed to prepare the sample and apply the indenter.
| Material | HK |
|---|---|
| Dentin | 68 |
| Gold foil | 69 |
| Tooth enamel | 343 |
| Quartz | 820 |
| Silicon carbide | 2480 |
| Diamond | 7000 |
Famous quotes containing the words hardness and/or test:
“Despots play their part in the works of thinkers. Fettered words are terrible words. The writer doubles and trebles the power of his writing when a ruler imposes silence on the people. Something emerges from that enforced silence, a mysterious fullness which filters through and becomes steely in the thought. Repression in history leads to conciseness in the historian, and the rocklike hardness of much celebrated prose is due to the tempering of the tyrant.”
—Victor Hugo (1802–1885)
“The test of a man’s or woman’s breeding is how they behave in a quarrel. Anybody can behave well when things are going smoothly.”
—George Bernard Shaw (1856–1950)