Low-alloy Steels
Low-alloy steels are usually used to achieve better hardenability, which in turn improves its other mechanical properties. They are also used to increase corrosion resistance in certain environmental conditions.
With medium to high carbon levels, low-alloy steel is difficult to weld. Lowering the carbon content to the range of 0.10% to 0.30%, along with some reduction in alloying elements, increases the weldability and formability of the steel while maintaining its strength. Such a metal is classed as a high-strength low-alloy steel.
Some common low alloy steels are:
- D6AC
- 300M
- 256A
| SAE designation | Composition |
|---|---|
| 13xx | Mn 1.75% |
| 40xx | Mo 0.20% or 0.25% or 0.25% Mo & 0.042% S |
| 41xx | Cr 0.50% or 0.80% or 0.95%, Mo 0.12% or 0.20% or 0.25% or 0.30% |
| 43xx | Ni 1.82%, Cr 0.50% to 0.80%, Mo 0.25% |
| 44xx | Mo 0.40% or 0.52% |
| 46xx | Ni 0.85% or 1.82%, Mo 0.20% or 0.25% |
| 47xx | Ni 1.05%, Cr 0.45%, Mo 0.20% or 0.35% |
| 48xx | Ni 3.50%, Mo 0.25% |
| 50xx | Cr 0.27% or 0.40% or 0.50% or 0.65% |
| 50xxx | Cr 0.50%, C 1.00% min |
| 50Bxx | Cr 0.28% or 0.50% |
| 51xx | Cr 0.80% or 0.87% or 0.92% or 1.00% or 1.05% |
| 51xxx | Cr 1.02%, C 1.00% min |
| 51Bxx | Cr 0.80% |
| 52xxx | Cr 1.45%, C 1.00% min |
| 61xx | Cr 0.60% or 0.80% or 0.95%, V 0.10% or 0.15% min |
| 86xx | Ni 0.55%, Cr 0.50%, Mo 0.20% |
| 87xx | Ni 0.55%, Cr 0.50%, Mo 0.25% |
| 88xx | Ni 0.55%, Cr 0.50%, Mo 0.35% |
| 92xx | Si 1.40% or 2.00%, Mn 0.65% or 0.82% or 0.85%, Cr 0.00% or 0.65% |
| 94Bxx | Ni 0.45%, Cr 0.40%, Mo 0.12% |
| ES-1 | Ni 5%, Cr 2%, Si 1.25%, W 1%, Mn 0.85%, Mo 0.55%, Cu 0.5%, Cr 0.40%, C 0.2%, V 0.1% |
Read more about this topic: Alloy Steel